High corner covering powder coating
Better corner coverage and masking performance;
Improves corner corrosion resistance;
HLS ACE-Standard series applied to 0.8mm chrome aluminum plate test plates (coating thickness 60-90 um)
| project | standard | HLS ACE-Standard Series |
| gloss | EN ISO 2813 (60°) | ≧90 |
| finish | visual | smooth |
| adhesion | EN ISO 2409 (2 mm) | Cross-cut rating Gt0 |
| impact resistance | ASTM D 2794 (15.9mm) punch diameter | More than 80 inches-pounds,pull adhesive tape , no film peeling |
| cupping tese | EN ISO 1520 | Indentation depth in excess 10mm ,no film cracking |
| bending performance | EN ISO 1519 | cylindrical axis bend test,passing 3mm axis diameter |
| film hardness | EN ISO 2815 | >85 Buckholz Hardness:>85 |
| Salt spray test | ASTM B 117 | After 500H ,no blistering ,no film peeling |
| humidity resistance | EN ISO 6270-2 | After 500H ,no foaming,no film peeling ,side corrosion max. 1mm |
| UV resistance | DIN EN ISO 11507 (UVB - 313) | Cycle: 50℃ UV 4 hours,40℃condensate 4 hours, no-powdering after 168H, excellent gloss retention and color stability |
| Accelerated weathering | DIN EN ISO 11507 (UVA – 340) | Cycle: 60℃UV 8 hours,45℃ condensate 4 hours, non-powdering after 500 hours, excellent gloss retention and color stability |
Note: If the surface is too small or unsuitable for instrument measurement, the workpiece can be compared with a model with a near gloss; For more technical details, please contact HLS customer service.
The following is the performance data for HLS ACE-Master series applied to the 0.8mm chrome aluminum plate test plate (coating thickness 60-90um).
| project | standard | HLS ACE-Master Series |
| gloss | EN ISO 2813 (60°) | ≧90 |
| appearance | visual | smooth |
| adhesion | EN ISO 2409 (2 mm) | Cross-cut rating Gt0 |
| impact resistance | ASTM D 2794 punch diameter (15.9mm) | More than 80 inches-pounds,pull adhesive tape , no film peeling |
| cupping tese | EN ISO 1520 | Indentation depth of more than 5mm ,no film cracking |
| bending performance | EN ISO 1519 | Cylindrical Mandrel bending test,passing 5mm Mandrel diameter |
| film hardness | EN ISO 2815 | >80 Buckholz Hardness:>80 |
| Resistant to mortar | EN12206-1 | The mortar is easy to remove, and the coating film adhesion and surface are free of damage. |
| Drilling,milling and sawing test | | No film breakage, peeling |
| NeutralSalt spray test | ASTM B 117 | After 1000 hours, no foaming, no paint film peeling. |
| humidity resistance | EN ISO 6270-2 | 1mm After 1000 hours, no foaming, no paint film peeling, and side corrosion max 1mm |
| Acetate mist test | ISO 9227 | After 1,000 hours testing – maximum 16 mm² infiltration over a scratch length of 10cm. |
| UV resistance | DIN EN ISO 11507 (UVB - 313) | Cycle: 50℃ UV 4 hours,40℃ condensate 4 hours. Non-powder after 300 hours of testing, excellent gloss retention and color stability. |
| Accelerated artificial aging | DIN EN ISO 11507 (UVA – 340) | Cycle: 60℃ UV 8 hours,45℃ condensate 4 hours. No chalking, excellent gloss retention and color stability after 1000 hours testing |
| Natural exposure | ISO 2810 (South Florida, latitude 27ºN) | After 12 months, No chalking, with excellent gloss retention and color stability. (southward 5°). |
Note: If the surface is too small or instrument measurement not suitable for it, the workpiece can be compared with a model with a near gloss; Meet with Qualicoat Class-1 product standards .For more technical details, please contact HLS customer service
The following is the performance data for HLS ACE-Premium Series applied to 0.8mm chrome aluminum plates (coating thickness 70-90um).
| project | standard | HLS ACE-Premium Series |
| gloss | EN ISO 2813 (60°) | ≧90 |
| adhesion | EN ISO 2409 (2 mm) | grid test Gt0 level |
| impact resisitance | ASTM D 2794 (5/8” ball) | 2.5Nm ,pass 2.5Nm pull adhesive tape , no film peeling |
| cupping tese | EN ISO 1520 | depth of impression 2mm film no cracking depth of impression 5mm pull adhesive tape , no film cracking |
| flexibilty | EN ISO 1519 | Cylindrical Mandrel bending test,mandrel diameter 2mm, film no cracking,dia 5mm, pull adhesive tape , no film peeling |
| film hardness | EN ISO 2815 | >80. Buckholz Hardness:>80 |
| Resistant to mortar | EN12206-1 | The mortar is easy to remove, and the coating film adhesion and surface are free of damage |
| Drilling,friction, sawing test | | No paint film cracking, peeling |
| Salt spray test | ASTM B 117 | no foaming and peeling after 3000H |
| Humidity resistance | EN ISO 6270-2 | no foaming and peeling after 3000H, and rust spot spread max 1mm |
| Acetic acid salt spray test | ISO 9227 | After 1,000 hours testing – maximum 16 mm² infiltration over a scratch length of 10cm. |
| UV resistance | DIN EN ISO 11507 (UVB - 313) | Cycle: 50℃ UV 4 hours,40℃ condensate 4 hours. Non-powder after 600 hours of testing, excellent gloss retention and color stability. |
| Accelerated artificial aging | DIN EN ISO 11507 (UVA – 340) | Cycle: 60℃ UV 8 hours,45℃ condensate 4 hours. Non-powder after 3000 hours of testing for excellent gloss retention and color stability |
| Natural exposure | ISO 2810 ( South Florida ,latutude 27°N ) | After 36 months, it is non-powdered, with excellent gloss retention and color stability. (southward 5°) |
Note: If the surface is too small or instrument measurement not suitable for it, the workpiece can be compared with a model with a near gloss; Meet with Qualicoat Class-2 product standards .For more information, please contact HLS customer service